VAUTID 145

VAUTID 145

For hardfacing layers with an extremely high level of wear resistance and good heat resistance properties

Carbides of tungsten, niobium and vanadium are some of the hardest and most effective particles available for wear protection. They are all combined in our tried-and-tested VAUTID 145. This alloy offers reliable protection against both extreme abrasion and high temperatures.

Recommended applications:

  • Components which are exposed to temperatures of up to 750°C.
  • Components which are subjected to very high levels of abrasive wear
    e.g. sinter crushers, glass recycling equipment, and the wear edges of excavator buckets and chain conveyors.
  • Components which are subjected to very high levels of abrasion at elevated temperatures, such as hot gas ventilation fans, hot dust ducts and blast furnace bell liners.

This welding alloy is also available as a VAUTID composite wear plate, produced using a special metal arc welding process (VAUTID VVP 145).

Wear resistance
Wear resistance

In abrasive applications, VAUTID 145 extends service life up to a factor of 14 compared to S235JR

Alloy
Typical microstructure VAUTID 145

Carbides
Chromium carbides Cr7C3 2200 HV1
Niobium carbides NbC 2400 HV1
Tungsten carbides W2C 3000 HV1
Vanadium carbides VC 3000 HV1

Typical microstructure VAUTID 145
Carbide hardness is specified in the [HV] unit (Vickers hardness).

Downloads
VAUTID material profile:
VAUTID ASW Auftragschweißwerkstoffe/Hardfacing welding consumables
VAUTID Hardfacing welding consumables
VAUTID material profile

Expert advice

For comprehensive technical advice with a personal touch, get in touch with VAUTID:

Sales Shanghai
Phone:+86 21 64824300
shanghai@vautid-group.com